Product Introduction
Gelatin-based high-strength hydrogel solution is composed of o-nitrobenzyl alcohol-modified gelatin (GelNB), methacrylated hyaluronic acid sodium salt (HAMA), photoinitiator (NAP) and phosphate aqueous solution. It is a sterile, ready-to-use hydrogel solution. This product inherits the excellent biocompatibility, cell adhesiveness and biodegradability of gelatin molecules. It can be used for cell surface culture, tissue engineering implants and other applications. Compared with traditional gelatin-based (GelMA) hydrogels, this material exhibits better elasticity and toughness, providing broad application prospects for tissue repair and regenerative medicine.
Product Specifications
Product Code
| Appearance
| Specification
| Note
|
G1518389
| Pale yellow transparent solution
| 5 mL/vial、10 mL/vial | Store in the dark |
Performance Parameters
| Item | Performance Parameter | Item | Performance Parameter |
| Tensile Modulus | 380~410 kPa | Elongation at Break | 168~180% |
| Tensile Strength | 1.7~2.0 MPa | Compressive Modulus | 550~690 kPa |
| Compressive Strength | 7.4~8.3 MPa | Water Content | ＞80% |
| Swelling Degree | 150~170% | Cytocompatibility | No potential cytotoxicity |
Instructions for Use
1. Heat the pre-filled syringe barrel at 37 ºC-60 ºC until the ink inside becomes a flowable liquid before use.
2. Before use, tighten the plunger to the rubber stopper inside the syringe, then unscrew the hard spiral rubber stopper to push out the solution for use.
3. The product undergoes cross-linking reaction to form a gel when irradiated with light at a wavelength of 365-405 nm.
Precautions
1. The product is sterilized. Please maintain aseptic operation during use to avoid microbial contamination.
2. Before use, the outer surface of the product syringe can be wiped and disinfected with alcohol.
3. The product must be stored strictly protected from light.