Carbon nanotube, single-walled, polyaminobenzene sulfonic acid functionalized - 75-85% carbon basis, D×L 1.1nm×0.5-1.0μm , bundle dimensions

Cat. No.: C466795

GRADE & PURITY 75-85% carbon basis, D×L 1.1nm×0.5-1.0μm , bundle dimensions

Synonyms

SWNT, PABS functionalized, Carbon nanotube, single-walled, PABS functionalized

Storage

Room temperature

Overview

Average diameter of individual SWCNT = 1.4nm ± 0.1nmMethod for dispersing in water: In solid form SWNTs are highly entangled and associated in macroscopic particles. It requires significant effort to break such an association and bring the material in solution. Sonicate 50 mg of material in 2 ml water for 30 min. Add 8 ml of water and sonicate for additional 90 min. Typically, after this procedure all material is completely dispersed according to visual observation. For quantitative measurement of the solubility, allow the dispersion to stand overnight at room temperature. Because of the high optical density of concentrated dispersion, dilute an aliquot from the upper layer of the studied dispersion by a factor of 100. The concentration of the diluted solution is estimated from the recorded NIR spectra using a plot of the absorbance at 9750 cm-1compared to the concentration of a standard solution (see reference).

Preparation instructions

Electric Arc Discharge Method

Specifications

Synonyms

SWNT, PABS functionalized, Carbon nanotube, single-walled, PABS functionalized

Specifications & Purity

75-85% carbon basis, D×L 1.1nm×0.5-1.0μm , bundle dimensions

Storage

Room temperature

Chemical and Physical Properties

• Solubility: ethanol: 0.05mg/mL; DMF: 0.1mg/mL; H2O: 5.0mg/mL (As determined by near-IR absorbance spectroscopy.)